ASTM A335 seamless ferritic alloy-steel pipe for high-temperature service. The pipe shall be suitable for bending, flanging (vanstoning), _and similar forming operations, _and for fusion welding. Grade P2 _and P12 steel pipes shall be made by coarse-grain melting practice.
Our products for ASTM A335 alloy steel pipes have been listed as follows:
The steel material shall conform to chemical composition, tensile property, _and hardness requirements. Each _length of pipe shall be subjected to the hydrostatic test. Also, each pipe shall be examined by a non-destructive examination method in accordance to the required practices. The range of pipe sizes that may be examined by each method shall be subjected to the limitations in the scope of the respective practices. The different mechanical test requirements for pipes, namely, transverse _or longitudinal tension test, flattening test, _and hardness _or bend test are presented.
Grade
|
C
|
Mn
|
P, S, max
|
Si
|
Cr
|
Mo
|
P11
|
0.05-0.15
|
0.30-0.60
|
0.025
|
0.50-1.00
|
1.00-1.50
|
0.44-0.65
|
P22
|
0.05-0.15
|
0.30-0.60
|
0.025
|
0.50 max
|
1.90-2.60
|
0.87-1.13
|
P5
|
0.15 max
|
0.30-0.60
|
0.025
|
0.50 max
|
4.00-6.00
|
0.45-0.65
|
P9
|
0.15 max
|
0.30-0.60
|
0.025
|
0.25-1.00
|
8.00-10.00
|
0.90-1.10
|
P91
|
0.08-0.12
|
0.30-0.60
|
0.020/0.010
|
0.20-0.50
|
8.00-9.50
|
0.85-1.05
|
V 0.18-0.25
|
N 0.03-0.07
|
Ni 0.40 max
|
Al 0.02 max
|
Nb 0.06-0.10
|
Ti 0.01 max
|
|
P92 |
0.07-0.13
|
0.30-0.60
|
0.020/0.010
|
0.50 max
|
8.50-9.50
|
0.30-0.60
|
V 0.15-0.25
|
N 0.03-0.07
|
Ni 0.40 max
|
Al 0.02 max
|
Nb 0.04-0.09
|
W 1.50-2.00
|
|
B 0.001-0.006
|
Ti 0.01 max
|
Zr 0.01 max
|
Grade P11, P22, P5, P9
|
Grade P91
|
Grade P92
|
|
Tensile strength, min, (MPa) |
415
|
585
|
620
|
Yield strength, min, (MPa) |
205
|
415
|
440
|
Elongation, min, (%), L/T |
30/20
|
20/…
|
20/…
|
Heat Treatment |
A / N+T
|
N+T / Q+T
|
N+T
|
Pipe may be either hot finished _or cold drawn with the finishing heat treatment noted below.